SS Stainless Steel Plate Sheet Supplier
Size: W*L(mm):
1250*1000-12000;
1500*1000-12000,
1800*1000-12000,
2000*1000-12000
Thickness: 0.25~150mm
Length: Less than 12m or as required or customized
Standards: ASTM,AISI,SUS,JIS,EN,DIN,BS,GB
Product Description
SS Stainless Steel Plate Sheet Supplier – BAOLAI
The stainless steel plate has a smooth surface, high plasticity, toughness and mechanical strength, and is resistant to corrosion by acids, alkaline gases, solutions and other media.
We offer high-quality stainless steel sheet/plate in various sizes and thicknesses with competitive prices.
| Material | 202 / 304 / 304L / 304H / 309S / 310S / 316 / 316L / 316Ti / 317L / 321 / 321H / 347 / 347H /410/ 410S/ 420/430/441/904L/Duplex,Hastelloy etc. |
| UNS No. – UNS S30400, UNS S30403, UNS S31008, UNS S31620, UNS S31603, UNS S31603, UNS S31635, UNS S31703, UNS S32100, UNS S34700, UNS S34709, UNS S8904 | |
| Surface Treatment | 2B, 2D, BA, NO. 1, NO. 4, NO. 8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, Titanium Coating, etc |
| Size | W*L(mm):1250*1000-12000;1500*1000-12000,1800*1000-12000,2000*1000-12000 |
| Thickness | 0.25~150mm |
| Length | Less than 12m or as required or customized |
| Standards | ASTM,AISI,SUS,JIS,EN,DIN,BS,GB |
Chemical Composition & Mechanical Property
| ASTM Grade | C | Si | Mn | P | S | Ni | Cr | Mo | |
| ASTM 201 | ≤0.15 | ≤1.00 | 5.50~7.50 | ≤0.060 | ≤0.03 | 1.00 ~1.50 | 13.50~15.00 | ||
| ASTM 202 | ≤0.15 | ≤1.00 | 7.50~10.00 | ≤0.060 | ≤0.03 | 4.00~6.00 | 17.00~19.00 | ||
| ASTM 304 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.00~11.00 | 18.00~20.00 | ||
| ASTM 304L | ≤0.035 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.00~13.00 | 18.00~20.00 | ||
| ASTM 316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00~14.00 | 16.00~18.00 | 2.00~3.00 | |
| ASTM 316L | ≤0.035 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00~14.00 | 16.00~18.00 | 2.00~3.00 | |
| ASTM 316L Ti | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00~14.00 | 16.00~18.00 | 2.00~3.00 | |
| ASTM 409L | ≤0.03 | ≤1.00 | ≤1.00 | ≤0.040 | ≤0.03 | 10.50~11.75 | |||
| ASTM 904L | ≤0.02 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.035 | 23.0-28.0 | 19.0-23.0 | 4.0-5.0 | |
| Mechanical Property | Grade of Material | Elongation (%) | Tensile Strength (Rm) N/m m³ | Yield Strength (Rp) 0.2%N/m m³ | Hardness (HV) | ||||
| ASTM 201 | ≥35 | ≥520 | ≥210 | ≤253 | |||||
| ASTM 202 | ≥35 | ≥590 | ≥210 | ≤218 | |||||
| ASTM 304 | ≥35 | ≥520 | ≥210 | ≤200 | |||||
| ASTM 304L | ≥35 | ≥480 | ≥180 | ≤200 | |||||
| ASTM 316 | ≥35 | ≥520 | ≥210 | ≤200 | |||||
| ASTM 316L | ≥35 | ≥480 | ≥180 | ≤200 | |||||
| ASTM 316Ti | ≥40 | ≥520 | ≥205 | ≤200 | |||||
| ASTM 409L | ≥25 | ≥360 | ≥175 | ≤175 | |||||
| ASTM 904L | ≥35 | ≥490 | ≥216 | ||||||
BAOLAI® Stainless (SS) steel sheets and plates application:
| Application | 1. Food processing equipment, particularly in beer brewing, milk processing & winemaking |
| 2. Kitchen benches, sinks, troughs, equipment, and appliances | |
| 3. Architectural paneling, railings & trim | |
| 4. Chemical containers, including for transport | |
| 5. Heat Exchangers | |
| 6. Woven or welded screens for mining, quarrying & water filtration | |
| 7. Pipe fittings, elbows, tee, reducer, flange, etc |
Surface Finish
The Difference Between 304 and 316 Stainless Steel
| 304 Stainless Steel | 316 Stainless Steel | |
| Description | Grade 304 stainless steel is generally regarded as the most common austenitic stainless steel. It contains high nickel content that is typically between 8 and 10.5 percent by weight and a high amount of chromium at approximately 18 to 20 percent by weight. Other major alloying elements include manganese, silicon, and carbon. The remainder of the chemical composition is primarily iron. | Similar to 304, Grade 316 stainless steel has high amounts of chromium and nickel. 316 also contains silicon, manganese, and carbon, with the majority of the composition being iron. A major difference between 304 and 316 stainless steel is the chemical composition, with 316 containing a significant amount of molybdenum; typically 2 to 3 percent by weight vs only trace amounts found in 304. The higher molybdenum content results in grade 316 possessing increased corrosion resistance. |
| Application | 1.The application requires excellent formability. The higher molybdenum content in Grade 316 can have adverse effects on formability. 2. The application has cost concerns. Grade 304 is typically more affordable than Grade 316. | 1. The environment includes a high amount of corrosive elements. 2. The material will be placed underwater or be exposed to water consistently. 3. In applications where greater strength and hardness are required. |